Antimicrobial alkali-silicate glass ceramic and the use thereof

ABSTRACT

The invention relates to a glass ceramic, wherein the initial glass comprises 30-65 percent (by weight) SiO 2 ; 5-30 percent (by weight) Na 2 O; 5-30 percent (by weight) CaO, and 0-15 percent (by weight) P 2 O 5 , and wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate. The invention is characterized in that either a glass ceramic with a single crystalline phase 1 Na 2 O-2 CaO-3 SiO 2  is excluded, or the crystalline size of the glass ceramic is &lt;10 μm, or the weight fraction of SiO 2  is &lt;47%.

The subject of this invention is a glass ceramic with an antimicrobial effect and/or a glass ceramic powder with an antimicrobial effect. The initial glass for the glass ceramic and/or the glass ceramic powder comprises 30-65 percent (by weight) SiO₂; 5-30 percent (by weight) Na₂O; 5-30 percent (by weight) CaO, and 0-15 percent (by weight) P₂O₅.

L L. Hensch, J. Wilson: An Introduction to Bioceramics, World Scientific Publ., 1993, describes glass that has a bioactive and partially antimicrobial effect as a bioglass. Such bioglass is characterized by the formation of hydroxyl apatite layers in aqueous media. Heavy metal-free alkali-alkaline earth-silicate glasses with antimicrobial properties are described in the DE-A-199 32 238 and DE-A-199 32 239 patent applications.

U.S. Pat. No. 5,676,720 discloses a glass powder that comprises 40-60 percent (by weight) SiO₂, 5-30 percent (by weight) Na₂O, 10-35 percent (by weight) CaO, and 0-12 percent (by weight) P₂O₅; furthermore, this patent also discloses glass ceramic that are made of a glass of this composition. However, U.S. Pat. No. 5,676,720 does not provide any information regarding the crystalline phase.

U.S. Pat. No. 5,981,412 describes a bioactive bioceramic material for medical applications with the crystalline phase Na₂O-2CaO-3SiO₂. The crystallite size is around 13 μm. The ceramization is performed by annealing for nucleation and crystallization. The main focus is on mechanical properties such as K_(1c). The crystalline phase portion is between 34 and 60 percent (by volume). U.S. Pat. No. 5,981,412 describes only a crystalline phase that is a high-temperature phase and that forms only under the special conditions indicated in this patent.

The technical task of the present invention is to provide a glass ceramic and/or powder made of such a glass ceramic that—as well as antimicrobial properties—also exhibits inflammation-inhibiting, skin-regenerating, and light-scattering properties.

The invention resolves this task by providing a glass ceramic in accordance with claim 1, wherein the main crystalline phase consists of alkali-alkaline earth-silicates and/or alkaline earth-silicates and/or alkali-silicates.

The glass ceramic and/or the glass ceramic powder as designed by this invention are characterized in that in the visible wavelength range they manifest a defined scattering and reflection effect. In cosmetic application, this effect can diminish the visual appearance of skin wrinkles. Furthermore, towards bacteria, fungi and viruses the glass ceramic demonstrates a biocidal and, definitely, a biostatic effect. However, in contact with humans, the glass ceramic is compatible with skin and is toxicologically harmless.

When used in the cosmetic field, the glass ceramic as designed by this invention has a maximum concentration of heavy metals of, for example, for Pb<20 ppm, Cd<5 ppm, As<5 ppm, Sb<10 ppm, Hg<1 ppm, Ni<10 ppm.

The initial unceramized glass that is used to produce the glass ceramic as designed by the invention contains between 30 and 65 percent (by weight) of SiO₂ as the network-forming ion. With a lower concentration, the propensity for spontaneous crystallization strongly increases, and the chemical resistance strongly decreases. With higher SiO₂ values, the crystallization stability level can decrease, and the processing temperature can grow significantly, so that the hot-forming properties deteriorate. In addition, SiO₂ is also a part of the crystalline phase that arises during the ceramization and must be contained in the glass in an accordingly high concentration if a high crystalline portion is to be created by the ceramization process.

Na₂O is used as the fluxing agent during the melting of glass. With a concentration of less than 5%, the melting process is negatively affected. Sodium is a part of the phases that form during the ceramization process, and thus must be contained in the glass in accordingly high concentrations if a high crystalline portion is to be created by the ceramization process.

K₂O acts as a fluxing agent during the melting of glass. Also, potassium is released in aqueous systems. If potassium is contained in the glass in a high concentration, potassium-containing phases such as potassium silicates are also released. The K₂O content can lie in the range of 0-40 percent (by weight), and preferably in the range of 0-25 percent (by weight), and especially preferred is the range of 0-10 percent (by weight).

The chemical resistance of the glass, and thus the ion release in aqueous media, is controlled by the P₂O₅ content. The P₂O₅ content is between 0 and 15 percent (by weight). With higher concentrations of P₂O₅, the hydrolytic resistance of the glass ceramic diminishes to an insufficient level.

In order to improve its meltability, the glass can contain up to 5 percent (by weight) of B₂O₃.

In order not to reach too great a degree of chemical resistance, the quantity of Al₂O₃ should be less than 3 percent (by weight). Al₂O₃ is used to control the chemical resistance of the glass.

In order to enhance the antimicrobial, and especially the antibacterial properties of the glass ceramic, ions with antimicrobial effects such as Ag, Au, l, Ce, Cu, Zn, Sn, can be incorporated in concentrations lower than 5 percent (by weight). Especially preferred is the addition of Ag. This allows for the formation (in the glass) of especially preferred crystalline phases, such as silver phosphates, e.g., AgPO₃ or silicon phosphates SiP₂O₇.

Furthermore, ions such as Ag, Cu, Au, and Li, can be incorporated as ingredients in order to control the high temperature conductivity of the molten charge, and thus to improve its meltability by means of a high-frequency melting process.

The concentration of these ions should be lower than 5 percent (by weight).

Coloring ions such as Fe, Cr, Co, and V can be incorporated, individually or in a combined fashion, in a total concentration of less than 1 percent (by weight).

The glass ceramic as designed by the invention is usually used in powder form. The ceramization can be done in the form of a glass block, a glass ribbon, or a glass powder. After ceramization, the glass ceramic blocks or ribbons must be ground to powder. If the powder has been ceramized, it must usually be ground again in order to eliminate agglomerates that have arisen during the ceramization process.

The decisive advantage of the ceramization in the powder form is a very small crystallite size that retains high overall phase portions. In addition, the crystallites grow from the surface of the surface defects that are produced by grinding.

The grinding process generates a large number of surface nuclei, so that many crystals start to grow at the same time, which allows one to obtain a very small crystallite size and, at the same time, a high crystalline phase portion. Therefore, no additional annealing treatment, as has been described in the U.S. Pat. No. 5,981,412 patent, is required to generate nuclei.

The grinding process can occur in dry, aqueous, or non-aqueous media.

Normally, the particle size is less than 500 μm. A useful particle size is <100 μm or <20 μm. Particle sizes that are <10 μm and smaller than 5 μm and smaller than 2 μm are especially useful. The particle size <1 μm has turned out to be exceptionally suitable.

In order to achieve certain effects, mixtures of various glass powders of different compositions from the indicated composition range and with different grain size are possible.

If a block or a ribbon of the initial glass is ceramized, and if crystalline portions of more than 30 percent (by weight) are endeavored, the crystallite sizes are larger than 10 μm. The crystallization occurs very quickly. The ceramization temperatures are between 50° C. and 400° C. above the glass transition temperature, and are preferably between 50° C. and 200° C. above the glass transition temperature, and are also preferably within a range of 50° C. and 100° C. Ceramization can be also performed in a multiple-stage thermal process. The crystallization process is primarily controlled from the surface. Needle-shaped crystals grow from the surface into the glass inside. A few crystals begin to grow in the glass inside. They are spheroidal. Needle-shaped crystals arise during the ceramization of a powder because of the large surface that is used for this process.

The ceramization of the initial glass is controlled from the surface. If, before the ceramization, the ribbons or blocks of the initial glass are ground into powder, the crystallization temperatures decrease significantly. The crystals begin to grow from the surfaces of the powder particles into their insides. The ceramization process can be controlled in such a manner that the particles have only an outer crystalline layer, whereas their insides remain amorphous. The selection of the particle size determines the mean crystal size.

The crystal phase portions in the glass after the ceramization are greater than 5 percent (by weight). Depending on the composition of the initial glass, up to almost 100 percent (by weight) of crystalline phase portions are achieved.

The preferred range is a phase portion between 10 and 30 percent (by weight). Even Still more preferable is the range above 50 percent (by weight).

Depending on the ceramization temperature, the ceramized powders are re-ground in order to again dissolve any agglomerations that have arisen during the ceramization process.

The main crystal phases are alkali-alkaline earth-silicates and/or alkaline earth silicates, especially NaCa silicates and Ca silicates, and these phase portions can be influenced by ceramization.

Other subsidiary crystal phases that can contain silver and/or phosphorus and/or silicon, such as AgPO3, SiP2O7, SiO2, can also occur, depending on the particular composition of the initial glass.

Phosphorus-containing glass ceramics from this range of composition can be bioactive in aqueous media; i.e., in aqueous systems they can form a hydroxyl apatite layer on their surface and also on foreign surfaces. Such powders are especially suitable as biomaterials, or they can be used in applications in which remineralization processes play an important role, such as in the fields of hair cosmetics, nail cosmetics, and tooth care.

Using the phases and phase portions, the chemical reactivity and/or the ion release can be influenced. Thus, chemical reactivity and ion releases can be controlled so that the main compatibility, the desired pH value and antimicrobial level, as well as the inflammation-inhibiting effect, can be tailored.

The crystalline phases demonstrate a significantly different chemical resistance than the glass phase. The chemical resistance can be both increased and decreased. Aside from chemical properties, depending on the main crystal phase properties, mechanical, abrasive, and optical properties can also be modified.

In the case of glass ribbons, at a relatively low ceramization temperature <₇₀₀° C., first one to two Na—Na silicates are formed. These are preferably (Na₂CaSi₃O₈/Na₂CaSiO₄/Na₂Ca₂(SiO₃)₃. Recrystallization occurs at temperatures higher than 700° C.

The resultant crystalline phases partially demonstrate a substantially higher water solubility than the glass phase. Thus, a special adjustment of the phase portions allows one to influence the ion release of the powder, as well as the pH value in an aqueous solution, and thus the biological effect.

The light-scattering effects that cause optical effects such as transparency, reflection, and light scattering, are induced by the different refractive indices of the glass phase and the crystal phase, as well as by the existing crystallite size.

During the dissolution of the crystalline phase in water or an aqueous solution, there remain honeycombed and/or porous surface structures that particularly influence the optical properties, such as transmission, reflection, and light scattering, of the powders in formulations. When solubilized in aqueous systems, the formation of nano particles is observed.

The glass ceramic powders are excellently suited for application in cosmetic products. Among others, these can be products in the field of color cosmetics. Also, the antimicrobial effect allows for application in the field of deodorants and antiperspirants. Moreover, hair and skin care provide other applications within the cosmetic field.

Due to its antimicrobial and inflammation-inhibiting properties, the powder is also suitable for use as an implant material in the medical field and particularly in the field of wound tending.

Furthermore, the material is suitable for use as a carrier substance in the production of artificial three-dimensional tissue structures.

In addition, the powder can be added to polymers, for example, as an antimicrobial active substance. Furthermore, such glass ceramic powders can be used in the fields of paints and lacquers, foodstuff, cleaning agents, paper hygiene, medical products, bioproducts, cosmetic products, and oral care.

The invention is described below using design examples and their attached figures.

FIG. 1 shows an X-ray diffraction diagram of an initial glass crystallized in powder form with a composition according to the design example 1, annealed for 5 hours at 650° C.

FIG. 2 shows an X-ray diffraction diagram of an initial glass crystallized in powder form, annealed for 5 hours at 590° C.

FIG. 3 shows an X-ray diffraction diagram of an initial glass crystallized in powder form, annealed for 5 hours at 560° C.

FIG. 4 shows a DTA analysis of an initial glass ceramized as a glass block according to design example 1.

FIG. 5 shows a DTA analysis of an initial glass ceramized in powder form according to design example 1.

FIG. 6 shows an X-ray diffraction diagram of glass ribbons ceramized at various temperatures according to design example 1.

FIG. 7 shows a high-temperature X-ray diagram of glass powders with a particle size of approximately 4 μm, depending on the temperature for glass ceramics with an initial glass according to design example 7.

FIG. 8 shows an X-ray diffraction diagram of a crystallized initial glass with a composition according to design example 8, annealed for 4 hours at 650° C.

FIG. 9 shows an X-ray diffraction diagram of a crystallized initial glass with a composition according to design example 8, annealed for 4 hours at 700° C.

FIG. 10 shows an X-ray diffraction diagram of a crystallized initial glass with a composition according to design example 8, annealed for 4 hours at 900° C.

FIG. 11 shows an X-ray diffraction diagram of a crystallized initial glass with a composition according to design example 9, annealed for 4 hours at 560° C.

FIG. 12 shows an X-ray diffraction diagram of a crystallized initial glass with a composition according to design example 9, annealed for 4 hours at 700° C.

FIG. 13 shows an X-ray diffraction diagram of a crystallized initial glass with a composition according to design example 9, annealed for 4 hours at 900° C.

FIG. 14 shows a DTA analysis of a initial glass ceramized as a glass block according to design examples 8 and 9.

FIG. 15 shows the standardized bacidity for a glass ceramic ceramized at various temperatures based on an initial glass with a composition according to design example 1

FIG. 16 shows the standardized conductivity for a glass ceramic ceramized at various temperatures based on an initial glass with a composition according to design example 1

FIG. 17 shows a SEM image of surface crystals on the surface of a glass ceramic that has been obtained by annealing an initial glass according to design example 1 at 660° C. for 4 hours.

FIG. 18 shows a SEM image of a section through a glass ceramic that has been obtained by means of bulk crystallization by annealing at T=660° C. for 4 hours.

FIG. 19 shows the surface of a glass ceramic ribbon ceramized at 700° C., and subsequently treated with water for 15 minutes.

FIGS. 20A-B show the surface of a glass ceramic ribbon ceramized at 700° C., and subsequently treated in water for 24 hours.

FIGS. 21A-B show the surface of a glass ceramic ribbon ceramized at 900° C., and subsequently treated in water for 24 hours.

A glass was produced by melting raw materials. The melting occurred in platinum crucibles at a temperature of 1550° C. Subsequently, the molten material was formed into ribbons. These ribbons were then further processed by dry grinding into a powder with a particle size of d50=4 μm.

Table 1 indicates the composition of the initial glasses in percent (by weight) for all glass ceramics described in the following text. TABLE 1 Composition (synthesis value) [In percent (by weight)] Ex- ample 1 2 3 4 5 6 7 8 9 10 11 SiO₂ 46.0 35 46 50 40 59 45 44.9 35 45 65 Al₂O₃ 0 0 0 0 0 0 1 0 0 0 0 CaO 25.0 29 20 10 25 20 25 24.5 29.0 23.5 10.0 MgO 0 0 0 0 0 0 0 0 0 0 0 Na₂O 25.0 30 20 25 25 20 24 24.5 29.5 24.5 20.0 K₂O 0 0 0 0 0 0 0 0 0 0 0 P₂O₅ 4.0 6 0 15 0 1 7 0 0 0 5.0 Ag₂O 0 0 0 0 0 0 0 0.1 0.1 0 0 ZnO 0 0 0 0 0 0 0 0 0 1.0 0

If we use the initial glasses indicated in Table for the production of glass ceramics, we discover that the glasses according the design examples 2 and 9 already demonstrate a strong propensity for crystallization during the melting process. Therefore, in the case of these initial glasses, it is necessary to cool them off especially quickly. If a partial or a complete ceramization already occurs during the melting of the glass, the glass ceramic can be subjected to a new annealing at the indicated temperatures in order to obtain the crystal phases described in this patent application.

FIGS. 1-3 show X-ray diffraction diagrams of initial glasses crystallized in powder form according to the design example 1 in Table 1, annealed for 5 hours at 650° C. (FIG. 1), 590° C. (FIG. 2), and 560° C. (FIG. 3). Clearly recognizable is the decrease in intensity of the diffraction orders 1 related to the crystal phases, which is synonymous with a decreasing crystal proportion in the glass ceramic.

For example, the intensity peaks can be ascribed to the Na₂CaSiO₄/Na₂OCaSiO₂ and Na₂CaSi₃O₈ crystal phases.

At higher temperatures, a recrystallization occurs, as is apparent from FIG. 6. At temperatures >900° C., Ca silicates can form, too. FIGS. 4 and 5 show the DTA analysis of an initial glass ceramized as a glass ribbon according to the design example 1 in Table 1 (FIG. 4), and an initial glass ceramized in powder form (FIG. 5) with a heating rate of 10 K/min. Clearly recognizable is the crystallization peak 3 for the crystal phase, whose temperatures are lower for the initial glass ceramized in powder.

FIG. 5 also shows the slightly exothermal reaction of the re-crystallization.

FIG. 7 shows high-temperature X-ray diagrams for a glass ceramic powder that has been obtained from an initial glass according to the design example 7, depending on the temperature. Re-crystallization occurs at higher temperatures (over 900° C.). The X-ray measurements were recorded during the heating process. At these temperatures, Ca silicates can also form. FIG. 7 shows 2000.1 and 2000.2, which according to the JCPDS database, designate the Na₂CaSiO₄ phase, and 2002.1 and 2002.2, which according to the JCPDS database designate the Na₂CaSi₃O₈ phase. As is apparent from FIG. 7, the Na₂CaSi₃O₈ phase forms only at a temperature above 900° C. The properties of various glass ceramics, produced in various different ways based on the initial glass according to the example 1 in Table 1, are indicated in Table 2. TABLE 2 Properties of glass ceramics according to the design example 1 Main Annealing Crystallite crystalline JCPDS time size phases Database Powder 580° C. 5 hours <0.5 Na₂CaSi₃O₈/ 12-0671/24- Na₂CaSiO₄ 10696 Na₂Ca₂(SiO₃)₃ Powder 650° C. 5 hours <1 Na₂CaSi₃O₈/ 12-0671/24- Na₂CaSiO₄ 10696 Na₂Ca₂(SiO₃)₃ Powder 700° C. 5 hours <15 Na₂CaSi₃O₈/ 12-0671/24- Na₂CaSiO₄ 10696 Na₂Ca₂(SiO₃)₃ Ribbons 700° C. 5 hours >100 μm Na₂CaSi₃O₈/ 12-0671/24- Na₂CaSiO₄ 10696 Na₂Ca₂(SiO₃)₃ Ribbons 600° C. 2 hours >20 μm Na₂CaSi₃O₈/ 12-0671/24- in volume Na₂CaSiO₄ 10696 Na₂Ca₂(SiO₃)₃

Table 3 shows the antibacterial effect of a glass ceramic powder that was annealed at 580° C. for 5 hours with a grain size of 4 μm. TABLE 3 Antibacterial effect of the powder according to Europ. Pharmakopoe (3. edition): Design example 1 (grain size 4 μm) P. E. coli aeruginosa S. aureus C. albicans A. niger Start 290,000 270,000 250,000 300,000 250,000  2 days 900 1,800 800 <100 2,000  7 days <100 200 <100 0 2000 14 days 0 0 0 0 0 21 days 0 0 0 0 0 28 days 0 0 0 0 0

No irritation has been determined by skin compatibility tests, i.e., oculsive tests over 24 hours.

Table 4 indicates in detail, and in a tabular form, exemplary main crystalline phases of Na—Ca silicate systems using the basic formula x Na₂O.y CaO.z SiO₂

and the numbers for x, y, and z. TABLE 4 Main Crystalline phase in Na—Ca silicate systems Na₂O CaO SiO₂ (x) (y) (z) 1 3 6 1 1 5 1 2 3 1 — 2 3 — 8 2 3 6 2 — 2 0 1 1 1 0 1

The results of the glass ceramics that have been obtained from the initial glasses according to design examples 8 and 9 are described in the following text.

FIGS. 8-10 show the X-ray diffraction diagrams of initial glasses crystallized in powder form according to the design example 8 in Table 1, and annealed for 4 hours at 560° C. (FIG. 8), 700° C. (FIG. 9), and 900° C. (FIG. 10). The phase determined from the intensity peaks is a Na—Ca silicate, namely Na₆Ca₃Si₆O₁₈ (JCPDS 77-2189) as a crystalline phase. Clearly recognizable is the change of the Na—Ca ratio in tandem with the increase in temperature.

FIGS. 11-13 show the X-ray diffraction diagrams of initial glasses crystallized in powder form according to the design example 9 in Table 1, and annealed for 4 hours at 560° C. (FIG. 11), 700° C. (FIG. 12), and 900° C. (FIG. 13). Two Na—Ca silicates Na₂CaSiO₄ (JCPDS 73-1726) and Na₂Ca₂SiO₇ (JCPDS 10-0016), as well as the silicon phosphate SiP₂O₇ (JCPDS 39-0189) and cristobalite SiO₂ (JCPDS 82-0512) can be identified in FIGS. 11-13 as the main crystalline phases. The samples produced at 700° C. and 900° C. that are shown in Tables 12 and 13 contain another crystalline phase, namely the silver phosphate AgPO₃ (JCPDS 11-0641). The portion of this phase is higher in the sample produced at 900° C. than in the sample produced at 700° C.

FIG. 14 shows the DTA thermo-analysis of an initial glass ceramized as a glass ribbon according to design examples 8 and 9 in Table 1 with heating rates of 10 K/min. The crystallization peak 3 for the crystal phase is clearly recognizable from design example 8 . The glass ceramic that is based on the initial glass according to design example 9 is a glass ceramic that has already been crystallized from the molten charge. No strong exothermal signal is observed in the DTA, because the subsequent crystallization or re-crystallization only releases a little heat. The reason for this phenomenon is that the initial glass in this design example has a propensity for spontaneous crystallization to occur during the melting process.

Table 5 shows the antibacterial properties of a glass ceramic powder that, based on an initial glass according to design example 8, was annealed at 560° C. with a grain size of 4 μm. TABLE 5 Antibacterial effect of powders according to Europ. Pharmakopoe (3. edition): Design example 8 annealed at 560° C. (grain size 4 μm) P. E. coli aeruginosa S. aureus C. albicans A. niger Start 290,000 270,000 250,000 300,000 250,000  2 days 700 2,000 500 <100 2,000  7 days 0 0 0 0 0 14 days 0 0 0 0 0 21 days 0 0 0 0 0 28 days 0 0 0 0 0

Table 6 shows the antibacterial properties of a glass ceramic powder that, based on an initial glass according to design example 9, was annealed at 900° C. with a grain size of 4 μm. TABLE 6 Antibacterial effect of powders according to Europ. Pharmakopoe (3. edition): Design example 9 (grain size 4 μm) P. E. coli aeruginosa S. aureus C. albicans A. niger Start 290,000 270,000 250,000 300,000 250,000  2 days 0 0 0 0 0  7 days 0 0 0 0 0 14 days 0 0 0 0 0 21 days 0 0 0 0 0 28 days 0 0 0 0 0

Table 7 indicates, in detail, and in a tabular form, the main crystalline phases found in the produced samples using the basic formula x Na₂O.y CaO.z SiO₂ and the numbers for x, y, and z.

Besides the Na—Ca phases, a silicon phosphate phase is also found. In addition, a silver phosphate phase is found at high temperatures above 700° C. TABLE 7 Main crystalline phases of the glass ceramics, design examples 8 and 9 Na₂O CaO SiO₂ (x) (y) (z) Ag₂O P₂O₅ Note 1 1 From 700° C. 3 3 6 1 1 1 1 2 1 1 1 2 1 3

Table 8 indicates the pH values and the conductivity of a 1% suspension of a glass ceramic powder that comprises an initial glass according to design example 7 in Table 1, for various annealing conditions for the production of glass ceramic. The annealing conditions include annealing time and annealing temperature. Depending on the annealing time and the annealing temperature, different main crystal phases develop in the glass ceramic. TABLE 8 pH value and conductivity of a glass ceramic powder that has crystallized from an initial glass according to design example 7 After 15 After 50 After 24 Annealing minutes Conductivity minutes Conductivity hours Conductivity conditions Ph value (μS/cm) Ph value (μS/cm) Ph value (μS/cm) Untreated 11.3 695 11.3 900 11.7 1,872 500° C. - 2 hours 11.1 526 11.2 623 11.4 1,054 600° C. - 2 hours 11.2 571 11.2 686 11.5 1,130 700° C. - 2 hours 11.2 576 11.2 679 11.5 1,007 800° C. - 2 hours 11.2 619 11.3 749 11.5 1,238 900° C. - 2 hours 11.3 859 11.4 949 11.6 1,288

FIGS. 15 and 16 show the pH value, i.e., the standardized bacidity and the standardized conductivity for a glass ceramic obtained by annealing for 2 hours at various temperatures based on an initial glass according to design example 1.

FIGS. 15 and 16 include the following reference numbers:

-   -   100: The unceramized initial glass according to design example 1     -   102: The initial glass according to design example 1 that has         been ceramized at 600° C. for 2 hours     -   104: The initial glass according to design example 1 that has         been ceramized at 700° C. for 2 hours     -   106: The initial glass according to design example 1 that has         been ceramized at 800° C. for 2 hours     -   108: The initial glass according to design example 1 that has         been ceramized at 900° C. for 2 hours

By standardized bacidity and standardized conductivity, we understand the bacidity and the conductivity standardized for the surface. These properties are independent of the actual particle size. Conductivity is indicated per surface (cm²) and mass (g) of powder.

Table 9 shows the ion release rate of an unceramized powder and glass ceramic powder in a 1% suspension that comprises, as the initial glass, a glass according to design example 7 in Table 1. The glass ceramic powder has been produced by annealing at a temperature of 650° C. for 4 hours. TABLE 9 Ion release rate (1% suspension, unit: mg/L) Not ceramized Powder ceramized at 650° C. Na 96.7 mg/Liter 63.2 mg/Liter Ca 29.8 mg/Liter 21.5 mg/Liter Si 63.5 mg/Liter 40.3 mg/Liter P 0.22 mg/Liter 0.67 mg/Liter pH 11.3 11.3 Conductivity  635 μS/cm  432 μS/cm

The following text describes the scanning of electron micrograph images (SEM images) of glass ceramics that have been obtained by crystallizing the initial glass according to design example 1.

FIG. 17 shows a SEM image of the surface of a glass ceramic that has been obtained by annealing an initial glass according to design example 1 at a temperature of 660° C. for 4 hours. The surface crystals on the ribbon are clearly recognizable. Parts of these surface crystals can be soluble in water so that, during a treatment with water, these crystals are dissolved, and a honeycomb structures remains. Furthermore, this crystalline surface can release certain phases, such as nano particles that, among other things, are important for applications in oral care, i.e., for the use of glass ceramic as designed by the invention in the field of tooth and oral care. Furthermore, the crystalline surface shown in this figure demonstrates light-scattering properties that can be used for certain applications.

While FIG. 17 shows the surface structure of the glass ceramic, FIG. 18 shows a SEM image of the crystallization inside the glass block, that is, the bulk crystallization. FIG. 17 is a section of FIG. 18. The section is marked in FIG. 18 with 3000. The glass ceramic shown in FIGS. 17 and 18 has been obtained by annealing [the initial glass] at a temperature of 660° C. for 4 hours. The formed crystallites in FIG. 18 are clearly recognizable as round points. The crystals formed in the bulk crystallization have light-scattering properties that can be used for certain applications. In FIGS. 17 and 18, crystallization occurred in the glass block (ribbon). Both FIGS. 17 and FIG. 18 show a cross-section of the surface of the block (ribbon). FIG. 17 is a section of FIG. 18, and shows the surface in detail.

FIG. 19 shows the surface of a glass ceramic ribbon that has been obtained by ceramizing an initial glass according to the design example 1 at 700° C. for 4 hours. The glass ceramic was subsequently treated with H₂O. The easily soluble crystalline phases essentially comprising Na—Ca silicate are dissolved. There remains a “honeycomb” structure that can be easily recognized in FIG. 19.

FIGS. 20A-B show the surface of a glass ceramic powder that has been obtained by ceramizing an initial glass according to design example 1 at 700° C. for 4 hours. The surface shown has been obtained by treating the glass ceramic powder with water for 24 hours.

Furthermore, we can recognize a certain surface coarseness in FIGS. 20A and 20B. As is apparent from the figures, the surface is relatively homogeneous, and does not show any formation of nano particles.

FIGS. 21A-B show the surface of a glass ceramic powder that has been obtained by ceramizing an initial glass according to design example 1 at a temperature of 900° C. for 4 hours. In contrast to the smooth surface obtained at lower annealing temperatures, as shown in FIGS. 20A and 20B, FIGS. 21A and 21B show the released nano crystals and a porous surface structure.

The crystalline nano particles are less soluble in water. The nano particles were formed during the annealing process, and have been released from the surface.

The released nano particles are important for, among other things, applications in oral care, because they have a desensitizing effect on the tooth nerve. The desensitizing effect is achieved in that the nano particles are able to close the tubulin channels.

The present invention provides a glass ceramic powder and a glass ceramic that can be used in a number of fields; for example, in the fields of cosmetics or food supplements, and in the medical field. 

1. Glass ceramic, wherein the initial glass comprises 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate, characterized in that the crystallite size is <0.1 μm.
 2. Glass ceramic, wherein the initial glass comprises 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate, characterized in that the glass ceramic is a glass ceramic powder that consists of glass ceramic particles, wherein the glass ceramic particles have a certain particle size, and the main crystalline phases have a crystallite size, wherein the ratio of crystallite size : particle size is <1:4, preferably <1:8.
 3. Glass ceramic according to claim 1, wherein the initial glass comprises: 30-<47 percent (by weight) of SiO₂ 10-30 percent (by weight) of Na₂O 10-30 percent (by weight) of CaO 2-15 percent (by weight) of P₂O₅.
 4. Glass ceramic according to claim 1, Characterized in that the main crystalline phases comprise sodium-potassium-silicate phases.
 5. Glass ceramic according to claim 1, characterized in that the crystalline phases are water-soluble sodium-calcium-silicate phases.
 6. Glass ceramic according to claim 1, characterized in that the initial glass further comprises 0-40, especially 0-25, and especially preferably 0-10 percent (by weight) of K₂O as well as 0-5 percent (by weight) of Al₂O₃.
 7. Glass ceramic according to claim 1, characterized in that the initial glass comprises 0-40 percent (by weight) of MgO and 0-50 percent (by weight) of B₂O₃.
 8. Glass ceramic according to claim 1, characterized in that the glass ceramic comprises metal ions with a total portion of <2 percent (by weight).
 9. Glass ceramic according to claim 8, characterized in that the metal ions include Ag, Au, l, Zn, Cu, and Ce.
 10. Glass ceramic powder that comprises a glass ceramic according to claim 1, wherein the particle size of the glass ceramic powder is <100 μm.
 11. Glass ceramic powder that comprises a glass ceramic according to claim 1, wherein the particle size of the glass ceramic powder is <20 μm.
 12. Glass ceramic powder that comprises a glass ceramic according to claim 1, wherein the particle size of the glass ceramic powder is <5 μm.
 13. Glass ceramic powder that comprises a glass ceramic according to claim 1, wherein the particle size of the glass ceramic powder is <1 μm.
 14. Method for the production of a glass ceramic powder according to claim 10, characterized in that the initial glass for the glass ceramic according to claim 1 is ground and subsequently a ceramization of the pulverized initial glass occurs.
 15. Use of a glass ceramic powder for use in cosmetic products for visual reduction of wrinkles, wherein the glass ceramic powder is obtained from a glass ceramic, and the initial glass of the glass ceramic comprises: 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate.
 16. Use of a glass ceramic powder for use in cosmetic products for the protection of skin from harmful UV radiation, wherein the glass ceramic powder is obtained from a glass ceramic, and the initial glass of the glass ceramic comprises: 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate.
 17. Use of a glass ceramic powder with antimicrobial effect in cosmetic products, wherein the glass ceramic powder is obtained from a glass ceramic, and the initial glass of the glass ceramic comprises: 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate.
 18. Use of a glass ceramic powder with antimicrobial effect in paints and lacquers, wherein the glass ceramic powder is obtained from a glass ceramic, and the initial glass of the glass ceramic comprises: 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate.
 19. Use of a glass ceramic powder with antinicrobial effect in medical products and preparations, wherein the glass ceramic powder is obtained from a glass ceramic, and the initial glass of the glass ceramic comprises: 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate.
 20. Use of a glass ceramic powder with antimicrobial effect in synthetic materials and polymers, wherein the glass ceramic powder is obtained from a glass ceramic, and the initial glass of the glass ceramic comprises: 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate.
 21. Use of a glass ceramic powder with antimicrobial effect in paper hygiene products, wherein the glass ceramic powder is obtained from a glass ceramic, and the initial glass of the glass ceramic comprises: 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate.
 22. Use of a glass ceramic powder with antimicrobial effect in foodstuff, wherein the glass ceramic powder is obtained from a glass ceramic, and the initial glass of the glass ceramic comprises: 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate.
 23. Use of a glass ceramic powder with antimicrobial effect in cleaning agents, wherein the glass ceramic powder is obtained from a glass ceramic, and the initial glass of the glass ceramic comprises: 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate.
 24. Use of a glass ceramic powder with antimicrobial effect in cleaning agents, wherein the glass ceramic powder is obtained from a glass ceramic, and the initial glass of the glass ceramic comprises: 30-<47 percent (by weight) of SiO₂ 5-30 percent (by weight) of Na₂O 5-30 percent (by weight) of CaO 0-15 percent (by weight) of P₂O₅, wherein the main crystalline phases comprise alkali-alkaline earth-silicate and/or alkali silicate and/or alkaline earth silicate. 